ABSTRACT
Experimental and theoretical models for formation of shrinkage defects during curing epoxy-amine systems under conditions of restricted shrinkage are analyzed in comparison with recent data obtained for the systems cured by anionic and radical polymerization. The resistance to formation of shrinkage defects was found to 200decrease for the systems cured by polycondensation, anionic, and radical polymerization, respectively.