ABSTRACT
Sustained load fracture is a general term for time-dependent crack growth under loading often well below that normally required to cause failure in a tensile or fracture toughness test. Examples of sustained load fracture are: • creep and creep crack growth • stress corrosion cracking • cracking due to embrittlement by internal or external (gaseous) hydrogen • liquid metal embrittlement.