ABSTRACT
The actual experimental moduli of the polymer materials are usually about only 1% of their theoretical values [1], while the calculated theoretical moduli of many polymer materials are comparable to that of metal or fiber reinforced composites, for instance, the crystalline polyethylene (PE) and polyvinyl alcohol have their calculated Young's moduli in the range of200-300 GPa, surpassing the normal steel modulus of 200 GPa. This has been attributed to the limitations of the folded-chain structures, the disordered alignment of molecular chains, and other defects existing in crystalline polymers under normal processing conditions.