chapter  9
Amorphous Metals Physical Properties
Pages 14

Ce60Al15Cu10Ni15 2 mm dia rods N 0.03-1 mN Increases (1) Dy3Al2 20 μm thick ribbons T 10−4 to 10−1 Decreases (2) Nd60Fe20Co10Al10 5 mm dia rods C 6 × 10−4 to 1 × 103 Increases (3) Pd40Ni40P20 5 mm dia rods C 3.3 × 10−5 to 2 × 103 Decreases (4) Pd80Si20 Ribbons T 10−4 to 10−2 No change (5) Ti40Zr25Ni8Cu9Be18 1 and 3 mm dia rods C 10−4 to 103 Increases (6) Ti45Zr16Ni9Cu10Be20 1 mm dia rods C 10−4 to 10−1 Increases (7) Zr41.25Ti13.75Cu12.5Ni10Be22.5 (Vit 1) 2.5 mm dia rods 102 to 104 No change (8) Zr41.25Ti13.75Cu12.5Ni10Be22.5 (Vit 1) 3.8-6.25 mm dia rods C 10−3 to 103 No change (9) Zr57Ti5Cu20Ni8Al10 3 mm dia rods C 1 × 10−4 to 3 × 103 Decreases (10) Zr60Ti14.7Nb5.3Cu5.6Ni4.4Be10 3 mm dia rods C 2 × 10−4 to 3.7 × 102 Increases (11) Zr65Al10Ni10Cu15 20 μm thick ribbons C 5 × 10−4 to 100 Increases (12) Zr65Al10Ni10Cu15 20 μm thick ribbons T 1.67 × 10−4 to 5 × 10−1 Increases (13)

Source: Data from Suryanarayana, C. and Inoue, A. Bulk Metallic Glasses, CRC Press, Boca Raton, FL, 2010. With permission.