Abstract ................................................................................................. 204 14.1 Introduction .................................................................................. 204 14.2 Experimental ................................................................................ 205 14.3 Results and Discussion ................................................................ 205 14.4 Conclusions .................................................................................. 212 Keywords .............................................................................................. 213 References ............................................................................................. 213
ABSTRACT
It has been shown that at semicrystalline polymers with devitrificated amorphous phase consideration as natural hybrid nanocomposites their anormalous high reinforcement degree is realized at the expense of crystallites partial recrystallization (mechanical disordering), that means crystalline phase participation in these polymers elastic properties formation. It is obvious, that the proposed mechanism is inapplicable for the description of polymer nanocomposites with inorganic nanofillers.