ABSTRACT
Failure stresses (GPa) for 64 single carbon fibers of length L = 10 mm [1–4] are given in Table 59.1. The two-parameter Weibull model was used for analysis [1]. Failure Stresses in GPa for 64 Carbon Fibers (L = 10 mm)
1.901
2.397
2.532
2.738
2.996
3.243
3.435
3.871
2.132
2.445
2.575
2.740
3.030
3.264
3.493
3.886
2.203
2.454
2.614
2.856
3.125
3.272
3.501
3.971
2.228
2.454
2.616
2.917
3.139
3.294
3.537
4.024
2.257
2.474
2.618
2.928
3.145
3.332
3.554
4.027
2.350
2.518
2.624
2.937
3.220
3.346
3.562
4.225
2.361
2.522
2.659
2.937
3.223
3.377
3.628
4.395
2.396
2.525
2.675
2.977
3.235
3.408
3.852
5.020