ABSTRACT
Failure stresses (GPa) for 66 single carbon fibers of length L = 50 mm [1–4] are given in Table 60.1. A two-parameter Weibull model was used for analysis [1]. Failure Stresses (GPa) for 66 Carbon Fibers (L = 50 mm)
1.339
1.807
1.974
2.172
2.335
2.471
2.633
3.042
1.434
1.812
2.019
2.180
2.349
2.497
2.670
3.116
1.549
1.840
2.051
2.194
2.356
2.514
2.682
3.174
1.574
1.852
2.055
2.211
2.386
2.558
2.699
1.589
1.852
2.058
2.270
2.390
2.577
2.705
1.613
1.862
2.088
2.272
2.410
2.593
2.735
1.746
1.864
2.125
2.280
2.430
2.601
2.785
1.753
1.931
2.162
2.299
2.431
2.604
2.785
1.764
1.952
2.171
2.308
2.458
2.620
3.020