ABSTRACT
The dynamic behaviours of several types of defects (single stacking faults, paired stacking faults, half loops of Shockley partial dislocation, misfit dislocations aligned along <310>) are analysed. Heating the sample up to 300°C causes the formation of a grid of edge dislocations. Finally, both heating and electron irradiation induce rapid degradation of the active layer.