ABSTRACT
Failure stresses (GPa) for 70 single carbon fibers of length L = 20 mm [1–4] are given in Table 61.1. The two-parameter Weibull model was used for analysis [1]. Failure Stress (GPa) for 70 Carbon Fibers (L = 20 mm)
1.312
1.966
2.224
2.382
2.554
2.726
3.012
1.314
1.997
2.240
2.382
2.566
2.770
3.067
1.479
2.006
2.253
2.426
2.570
2.773
3.084
1.552
2.021
2.270
2.434
2.586
2.800
3.090
1.700
2.027
2.272
2.435
2.629
2.809
3.096
1.803
2.055
2.274
2.478
2.633
2.818
3.128
1.861
2.063
2.301
2.490
2.642
2.821
3.233
1.865
2.098
2.301
2.511
2.648
2.848
3.433
1.944
2.140
2.339
2.514
2.684
2.880
3.585
1.958
2.179
2.359
2.535
2.697
2.954
3.585