ABSTRACT
General formulae are derived for the activation energy of cross-slip of Shockley partial dislocations via the stair-rod mode. It is shown that local stress concentration due to a pile-up or a microtwin tip makes such a cross-slip process easier. As an example of illustration, zigzag propagation of deformation microtwins across the domain structure in ordered Ni3V alloys is discussed.