ABSTRACT
Teodoriu et al., (2012) performed unconfined and confined compression tests on cubic samples to determine the mechanical properties of cement class G. The uniaxial compressive strength and Young’s modulus of cement class G cured at 65°C was measured as 64 MPa and 16 GPa respectively. The compressive strength of the cement class G cured at 100°C and 18 MPa was recorded as 47 MPa.