ABSTRACT
The in-plane structure of intercalated TiOFy was determined by electron dif fraction and a typical pattern is shown in Fig. 13. It shows the formation of a TiOFy superlattice having two preferential rotational orientations with respect to the graphite lattice of 19.3 ± 2.8° around the [001] axis [51].