ABSTRACT
In this chapter, the matrix cracking closure behavior in high-temperature ceramic-matrix composites (CMCs) was investigated. A hysteresis-based identification method was developed to determine the matrix cracking closure stress using the damage parameter of interface reverse slip ratio. The cracking closure stress in different CMCs was determined and the effects of fiber volume fraction, interface shear stress, and thermal residual stress on the cracking closure stress were also discussed.