The Si substrate was micromachined based on photolithography; see Figure 2.1 for the process steps of a standard one-mask Si-micromachining process.3 After photolithography, the exposed portions of photoresist were dissolved by a developer solution, and the remaining unexposed areas were hardened by heating (baking). The exposed areas of the Si substrate were etched subsequently.